Abstract
The effects of composition, temperature, and frequency-dependent dielectric properties of barium-nickel-based ferrites have been investigated. The conventional ceramic technique prepared the compositions BaNi2-xZnxFe16O27 (at x = 0.0, 0.4, 1.2, and 2). The analysis of X-ray diffraction patterns showed that they were single-phase. The average grain size, lattice constant, and density were found to increase as Zn2+ ion substitution increased. According to the frequency and Zn concentration, the dielectric parameters were properly set. Overall, the dielectric properties of this sample make them a suitable candidate for flexible supercapacitors and are best suited for high-frequency region applications. The initial magnetic permeability of the prepared sample was increasing as the Zn ion contents increases. The produced samples were suitable for application as microwave absorbers, data storage appliances, and magnetic recording mediums.