Nadia.A.Ai* Seenaa I.Hussein Mohammed K .Jawad Ikram A. AL-Ajaj
الملخص الانجليزي
A growing need for materials with good tribological and mechanical properties led to prepare , characterize and
measure wear, hardness and impact properties of epoxy (EP) with different weight percentage of SiO2 and Al2O3
nano particles (0.5%, 1%,1.5%,2%,2.5%,3%) . Silica and alumina nanoparticles have average diameter size
16.69 and 46.73 nm respectively measured by scanning probe microscope.A combination of two different
techniques (high shear mixing followed by ultrasonication) was used to prepared the nanocomposites. Fourier
transition infrared (FTIR) was used to characterize the nanoparticles (Al2O3 an SiO2) .Wear rate, hardness and
impact energy properties were measured for EP/ Al2O3, EP/ SiO2 nanocomposites . Decreasing in wear values
with addition of nanoparticles ( especially nano Al2O3) were observed. Approximately 30% and 80% increasing
in hardness values and impact energy were observed. An enhancement in whole measurement for all composites
was observed, yet (EP/ Al2O3, EP/ SiO2) composites with 2.5%nano Al2O3 show in general better hardness and
impact results.
words:
سيناء ابراهيم حسين | Seenaa Ibraheim Hussein | 5625