عنوان المقالة:Structural, Optical and electrical characteristics of sulfur incorporated ZnSe thin films Structural, Optical and electrical characteristics of sulfur incorporated ZnSe thin films
جمعه عبدالجواد محمد على | Gomaa A. M. Ali | 20567
نوع النشر
مجلة علمية
المؤلفون بالعربي
E.R. Shaaban, A. Almohammedi, El Sayed Yousef, Gomaa A.M. Ali, Kwok Feng Chong, A. Adel, A. Ashour
المؤلفون بالإنجليزي
E.R. Shaaban, A. Almohammedi, El Sayed Yousef, Gomaa A.M. Ali, Kwok Feng Chong, A. Adel, A. Ashour
الملخص العربي
In the present study, polycrystalline materials of ZnSe1-xSx (x = 0, 0.25, 0.5, 0.75 and 1) were prepared by a conventional solid-state reaction method. Thin films of ZnSe1-xSx of about 1 µm have been produced using evaporation method. The importance of ZnSe1-xSx compound is the tunability of band gap when incorporating S into the ZnSe. Adding S at the expense of Se in ZnSe to form Zn-Se-S, which has a wider energy gap window layer to permit more light to reach the junction of solar cell. Both of optical constants (n, k) and film thickness have been determined precisely in terms of envelop method. Optical absorption spectra showed that band gap values increase with increasing S content. The electrical conductivity of ZnSe1-xSx was studied and exhibit two type of variation versus temperature. The activation energy of linear portion of the low temperature range is lower than the activation energy of linear portion of high temperature range and it increases with increasing the sulfur content in all films in both temperature ranges.
الملخص الانجليزي
In the present study, polycrystalline materials of ZnSe1-xSx (x = 0, 0.25, 0.5, 0.75 and 1) were prepared by a conventional solid-state reaction method. Thin films of ZnSe1-xSx of about 1 µm have been produced using evaporation method. The importance of ZnSe1-xSx compound is the tunability of band gap when incorporating S into the ZnSe. Adding S at the expense of Se in ZnSe to form Zn-Se-S, which has a wider energy gap window layer to permit more light to reach the junction of solar cell. Both of optical constants (n, k) and film thickness have been determined precisely in terms of envelop method. Optical absorption spectra showed that band gap values increase with increasing S content. The electrical conductivity of ZnSe1-xSx was studied and exhibit two type of variation versus temperature. The activation energy of linear portion of the low temperature range is lower than the activation energy of linear portion of high temperature range and it increases with increasing the sulfur content in all films in both temperature ranges.
تاريخ النشر
15/03/2018
الناشر
Optik
رقم المجلد
رقم العدد
رابط خارجي
https://www.sciencedirect.com/science/article/pii/S0030402618303115
الكلمات المفتاحية
ZnSeS; Thin Films; Optical Constants; Tunable energy Gap; Electrical conductivity