Aluminum-lithium alloys used in the aerospace industry as structural components
and strengthened by age-hardening. This study aims to improve properties of Al-Li
alloys such as strength, behavior hot rolling and addition element, i.e. Mg and Cu to
this alloy. Several tests were carried out to evaluate the performance of alloy, such as
hardness, tensile, and microstructure by OP, SEM and XRD. Result showed that
addition 3.2% Cu to base alloy improve strength from (62MPa) to (78MPa) when
aging at 175°C.and improve hardness from (97.3 Hv) to (119.79Hv) At the same
temperature. But the improvement is great when addition 0.6% Mg to base alloy
improve tensile strength from (62MPa) to (124MPa) at the same time improved
hardness from (119.79Hv) to (152.96Hv) at the same temperature.