عنوان المقالة:Electrocatalytic activity of CoFe1.9Mo0.1O4-Ce0.8Gd0.18Ca0.02O2-δ composite cathode for ammonia synthesis from water and nitrogen Electrocatalytic activity of CoFe1.9Mo0.1O4-Ce0.8Gd0.18Ca0.02O2-δ composite cathode for ammonia synthesis from water and nitrogen
Purpose
This paper aims to investigate the electrocatalytic activity of CoFe1.9Mo0.1O4-Ce0.8Gd0.18Ca0.02O2-δ composite (CFMo-CGDC) for the direct synthesis of ammonia from H2O and N2 under atmospheric pressure.
Designs
CoFe1.9Mo0.1O4 nanoparticles (CFMo NPs) were synthesized via a sol-gel method. CFMo NPs were characterized using X-ray diffraction (XRD), Brunauer–Emmet–Teller (BET) specific surface area measurement and scanning electron microscope (SEM). Double-chamber reactor was used to synthesize ammonia using H2O and N2 as precursors. The factors affecting the ammonia formation rate (applied voltage and temperature) were studied.
Findings
CoFe1.9Mo0.1O4 nanoparticles (CFMo NPs) were synthesized via a sol-gel method. CFMo NPs were characterized using XRD, Brunauer–Emmet–Teller (BET) specific surface area measurement and SEM. Double-chamber reactor was used to synthesize ammonia using H2O and N2 as precursors. The factors affecting the ammonia formation rate (applied voltage and temperature) were studied.
Originality/value
The usage of CFMo-CGDC composite as an electrocatalyst for the synthesis of ammonia directly from H2O and N2.
الملخص الانجليزي
Purpose
This paper aims to investigate the electrocatalytic activity of CoFe1.9Mo0.1O4-Ce0.8Gd0.18Ca0.02O2-δ composite (CFMo-CGDC) for the direct synthesis of ammonia from H2O and N2 under atmospheric pressure.
Designs
CoFe1.9Mo0.1O4 nanoparticles (CFMo NPs) were synthesized via a sol-gel method. CFMo NPs were characterized using X-ray diffraction (XRD), Brunauer–Emmet–Teller (BET) specific surface area measurement and scanning electron microscope (SEM). Double-chamber reactor was used to synthesize ammonia using H2O and N2 as precursors. The factors affecting the ammonia formation rate (applied voltage and temperature) were studied.
Findings
CoFe1.9Mo0.1O4 nanoparticles (CFMo NPs) were synthesized via a sol-gel method. CFMo NPs were characterized using XRD, Brunauer–Emmet–Teller (BET) specific surface area measurement and SEM. Double-chamber reactor was used to synthesize ammonia using H2O and N2 as precursors. The factors affecting the ammonia formation rate (applied voltage and temperature) were studied.
Originality/value
The usage of CFMo-CGDC composite as an electrocatalyst for the synthesis of ammonia directly from H2O and N2.
إبراهيم علي أحمد عمار | Ibrahim Ali Ahmed Amar | 14916