عنوان المقالة: effect of AL2O3 and SIO2 nanopartical on wear, hardness and impact behavior of epoxy composites
سيناء ابراهيم حسين | Seenaa Ibraheim Hussein | 5430
- نوع النشر
- مقال علمي
- المؤلفون بالعربي
- المؤلفون بالإنجليزي
- Nadia.A.Ai* Seenaa I.Hussein Mohammed K .Jawad Ikram A. AL-Ajaj
- الملخص الانجليزي
- A growing need for materials with good tribological and mechanical properties led to prepare , characterize and measure wear, hardness and impact properties of epoxy (EP) with different weight percentage of SiO2 and Al2O3 nano particles (0.5%, 1%,1.5%,2%,2.5%,3%) . Silica and alumina nanoparticles have average diameter size 16.69 and 46.73 nm respectively measured by scanning probe microscope.A combination of two different techniques (high shear mixing followed by ultrasonication) was used to prepared the nanocomposites. Fourier transition infrared (FTIR) was used to characterize the nanoparticles (Al2O3 an SiO2) .Wear rate, hardness and impact energy properties were measured for EP/ Al2O3, EP/ SiO2 nanocomposites . Decreasing in wear values with addition of nanoparticles ( especially nano Al2O3) were observed. Approximately 30% and 80% increasing in hardness values and impact energy were observed. An enhancement in whole measurement for all composites was observed, yet (EP/ Al2O3, EP/ SiO2) composites with 2.5%nano Al2O3 show in general better hardness and impact results. words:
- تاريخ النشر
- 20/04/2015
- الناشر
- Chemistry and Materials Research
- رقم المجلد
- 7
- رقم العدد
- 4
- رابط الملف
- تحميل (92 مرات التحميل)
- رابط خارجي
- https://pdfs.semanticscholar.org/b472/c1dee369bdc44f242a7200dc3b48ebb85f44.pdf
- الكلمات المفتاحية
- Nanoparticles, Nanocomposites, wear, Impact, hardness.y