- In this research prepartion of curcumin-silica materials using sol-gel method (bio-based materials)by reaction phenolic hydroxy group of curcumin with silanol group of silica . Tetraethoxysilane (TEOS ) was used as the silica precursor, hydrochloric acid (HCl) ,as the catalyst .Curcumin form as the organic precursor, Curcumin was dissolved in THF ( concentration of 10 wt%). 1 gm curcuim dissolved 10 ml THF , The mixture was stirred under nitrogen until the curcumin dissolved completely to give a clear yellow solution. TEOS + HCl (0.1M) ) solution was added drop by drop to the cucumin solution under continuous stirring to give four different organic/inorganic ratios (15%,25%,35%, and 50% v/v). The results show that the absorption peak shift with red shift and the Fluorescence Spectrophotometer ,silica-curcumin materials were showed ablue shifted peak. DTA thermograph shows sharp endothermic peak this can be attributed to the vaporization of water and ethanol. I.
- تاريخ النشر
- 21/02/2015
- الناشر
- International Journal of Advanced Research in Science, Engineering and Technology
- رقم المجلد
- 2
- رقم العدد
- 12
- رابط الملف
- تحميل (92 مرات التحميل)
- الكلمات المفتاحية
- : Silica,Curcumin ,Sol-Gel,FTIR,UV.VIS.,DTA