عنوان المقالة:Electrochemical synthesis of ammonia based on a carbonate-oxide composite electrolyte Electrochemical synthesis of ammonia based on a carbonate-oxide composite electrolyte
إبراهيم علي أحمد عمار | Ibrahim Ali Ahmed Amar | 13551
نوع النشر
مجلة علمية
المؤلفون بالعربي
Ibrahim A Amar, Rong Lan, Christophe TG Petit, Valeria Arrighi, Shanwen Tao
المؤلفون بالإنجليزي
Ibrahim A Amar, Rong Lan, Christophe TG Petit, Valeria Arrighi, Shanwen Tao
الملخص الانجليزي
Electrochemical synthesis of ammonia based on carbonate electrolyte is presented in this paper. Spinel oxide CoFe2O4 was synthesised via a co-precipitation method and characterised by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Ammonia was successfully synthesised from hydrogen and nitrogen under atmospheric pressure using CoFe2O4as catalyst (primary particle size 10–20 nm) together with silver at the cathode, Ag–Pd at the anode and carbonate-LiAlO2 composite as electrolyte respectively. Ammonia formation was observed at 400, 425 and 450 °C and the maximum rate of ammonia production was found to be 2.32 × 10−10 mol s−1 cm−2 at 400 °C and 0.8 V. The AC impedance measurements were recorded before and after the ammonia synthesis at 400, 425 and 450 °C. The electrolytic cell during the ammonia synthesis process was more stable at 450 °C and 0.8 V over a period of 2 h. This experiment also indicates that the carbonate-LiAlO2 composite electrolyte exhibits proton conduction.
تاريخ النشر
03/02/2011
الناشر
Solid State Ionics
رقم المجلد
182
رقم العدد
1
رابط DOI
https://doi.org/10.1016/j.ssi.2010.11.009
الصفحات
133-13
رابط خارجي
https://www.sciencedirect.com/science/article/abs/pii/S0167273810006314
الكلمات المفتاحية
Electrochemical synthesis of ammonia, Carbonate Proton conduction , CoFe2O4 Spinel catalyst, Impedance spectroscopy
رجوع