عنوان المقالة:Preparation of dense La0.5Sr0.5Fe0.8Cu0.2O3−δ–(Li,Na)2CO3–LiAlO2 composite membrane for CO2 separation Preparation of dense La0.5Sr0.5Fe0.8Cu0.2O3−δ–(Li,Na)2CO3–LiAlO2 composite membrane for CO2 separation
إبراهيم علي أحمد عمار | Ibrahim Ali Ahmed Amar | 13549
نوع النشر
مجلة علمية
المؤلفون بالعربي
Rong Lan, Sami M. M. Abdallah, Ibrahim A. Amar, Shanwen Tao
المؤلفون بالإنجليزي
Rong Lan, Sami M. M. Abdallah, Ibrahim A. Amar, Shanwen Tao
الملخص الانجليزي
Dense La0.5Sr0.5Fe0.8Cu0.2O3−δ–(Li,Na)2CO3 and La0.5Sr0.5Fe0.8Cu0.2O3−δ–(Li,Na)2CO3–LiAlO2 composite membranes were prepared for CO2 separation. The La0.5Sr0.5Fe0.8Cu0.2O3−δ (LSFCu) was prepared via the combined EDTA–citrate complex sol–gel process according to a previous study and then used in the synthesis of the dual phase membrane. XRD characterisation of the La0.5Sr0.5Fe0.8Cu0.2O3−δ sample showed it is orthorhombic structure with space group , a=5.4784(5) Å, b=7.7456(7) Å, c=5.5014(5) Å, and V=233.44(4) Å3. Dense composite membrane was obtained after carbonate treatment. Mixed CO2/N2, CO2/O2 and CO2/air gases were used for CO2 permeation experiments. At 750 °C, high CO2 permeation rate of 1.55 ml cm−2 min−1 was observed for the LSFCu–(Li,Na)2CO3–LiAlO2 composite membrane when 20% CO2/80% O2 mixture was used as the feed gas. Introduction of ~10 wt% LiAlO2 in the oxide–carbonate composite results in increased CO2 permeation rates which is likely due to the enhancement in surface reaction. The dominant pathway for CO2 permeation in the LSFCu–(Li,Na)2CO3–LiAlO2 composite membrane was believed through the coherent interaction between O2− and ions. Increased oxygen partial pressure in the feed gas can facilitate CO2 permeation. Due to the low O2 concentration in real flue gases, potentially the LSFCu–(Li,Na)2CO3–LiAlO2 dual phase membrane will separate CO2 only which provides an alternative technology for CO2 separation.
تاريخ النشر
15/10/2014
الناشر
Journal of Membrane Science
رقم المجلد
468
رقم العدد
ISSN/ISBN
0376-7388
رابط DOI
https://doi.org/10.1016/j.memsci.2014.06.030
الصفحات
380-388
رابط خارجي
https://www.sciencedirect.com/science/article/abs/pii/S0376738814004815
الكلمات المفتاحية
CO2 separation, Membrane separation, Carbonate, Oxide, (Li,Na)2CO3