عنوان المقالة:Ammonia Synthesis From Water and Nitrogen Using Lanthanum-Doped Strontium Titanate/Gadolinium And Calcium Co-Doped Ceria Composite-Based Electrocatalyst Ammonia Synthesis From Water and Nitrogen Using Lanthanum-Doped Strontium Titanate/Gadolinium And Calcium Co-Doped Ceria Composite-Based Electrocatalyst
إبراهيم علي أحمد عمار | Ibrahim Ali Ahmed Amar | 12360
نوع النشر
مجلة علمية
المؤلفون بالعربي
ابراهيم علي عمار
المؤلفون بالإنجليزي
Ibrahim A. Amar
الملخص العربي
Electrochemical synthesis of carbon-free ammonia from H2O and N2 is a promising technology for reducing global CO2 emissions from the Haber-Bosch process (industrial ammonia production process). This study aims to explore the electrocatalyst activity of non-noble metal perovskite-based catalyst (La0.3Sr0.7TiO3-Ce0.8Gd0.18Ca0.02O2-δ, LST-CGDC) for ammonia synthesis from wet nitrogen (3% H2O). LST was prepared via a sol-gel process and characterized using X-ray diffraction (XRD). Ammonia was successfully synthesized in a double-chamber reactor, with a maximum ammonia formation rate of about 7 × 10-11 mol s-1 cm-2 and Faradaic efficiency of 0.2% at 400 °C and 1.4 V. The results demonstrated that direct ammonia synthesis from water and nitrogen is a promising green and sustainable ammonia synthesis technology.
الملخص الانجليزي
Electrochemical synthesis of carbon-free ammonia from H2O and N2 is a promising technology for reducing global CO2 emissions from the Haber-Bosch process (industrial ammonia production process). This study aims to explore the electrocatalyst activity of non-noble metal perovskite-based catalyst (La0.3Sr0.7TiO3-Ce0.8Gd0.18Ca0.02O2-δ, LST-CGDC) for ammonia synthesis from wet nitrogen (3% H2O). LST was prepared via a sol-gel process and characterized using X-ray diffraction (XRD). Ammonia was successfully synthesized in a double-chamber reactor, with a maximum ammonia formation rate of about 7 × 10-11 mol s-1 cm-2 and Faradaic efficiency of 0.2% at 400 °C and 1.4 V. The results demonstrated that direct ammonia synthesis from water and nitrogen is a promising green and sustainable ammonia synthesis technology.
تاريخ النشر
07/01/2023
الناشر
Biointerface Research in Applied Chemistry
رقم المجلد
13
رقم العدد
5
ISSN/ISBN
2069-5837
رابط DOI
10.33263/BRIAC135.402
الصفحات
402
رابط الملف
تحميل (0 مرات التحميل)
رابط خارجي
https://biointerfaceresearch.com/?page_id=11224
الكلمات المفتاحية
Ammonia electrosynthesis; water; nitrogen; lanthanum-doped strontium titanate; redox stable perovskite oxide; carbon-fee synthesis; composite cathodes
رجوع