The non-uniform stress distribution occurs in a tension member adjacent to a connection, in which all elements of the cross-section are not directly connected.

This effect reduces the member’s design strength because the entire cross-section is not fully effective in the critical section’s location. That's why an experimental study has been done to investigate the effect of the weld length on the tension capacity, two specimens (hollow structural sections) have been tested by using Instron 8800 machine with two weld lengths, 46 mm and 56 mm. The 46 mm size is the minimum requirement of the sufficient size of the tension connection depending on United States Steel Standard. The Result proved that there has been too much effect on the connection carrying tension capacity. The result of the 46 mm weld length is about 155 KN and about 180 KN for the 56 mm weld length. While the ABAQUS simulation results were about 168 KN for the 46 mm weld length and about 172 KN for the 56 mm weld length.

توزيع الإجهاد يكون غير منتظم في مقطع التوتر (الشّد) خاصة في مناطق اللحام حيث تكون جميع عناصر المقطع غير متصلة بشكل مباشر.

يقلل هذا التأثير من القوة التصميمية للمقطع، بسبب أن المقطع العرضي بأكمله غير فعّال بشكل كامل في موقع الجزء الحرج، لهذا السبب تم إجراء دراسة تجريبية لعينتين من أقسام هيكلية مجوفة (hollow structural sections ) باستخدام آلة INSTRON باستخدام طولين مختلفين للحام لدراسة تأثير طول اللحام على القوة التصميمة باستخدام طول لحام 46 ملم و 56 ملم، وأثبتت النتيجة ذلك التأثير الكبير لطول اللحام على قدرة الشّد التصميمية، حيث بلغت سعة الشد حوالي 155 كيلو نيوتن لنموذج ذو طول 46 ملم، في حين بلغت سعة الشد حوالي 180 كيلو نيوتن للنموذج الثاني ذو طول لحام 56 ملم. في حين وصلت قيمة سعة الشد في عملية المحاكاة في برنامج الـ ABAQUS إلى 168 كيلو نيوتن لنموذج ذو طول 46 ملم وحوالي 172 كيلو نيوتن للنموذج الثاني ذو طول لحام 56 ملم.